T300 Polyurea antiseptic coating
Basic Info
Model No.: T300
Product Description
T300 Polyurea antiseptic coating
Product introduction polyaspartic polyurea
Steel structures such as petrochemical storage tanks, chemical pipelines, offshore oil platforms, and port engineering are exposed to harsh atmospheric corrosive environments and are subject to corrosion by corrosive factors such as moisture, oxygen, coastal salt spray, and chemical atmosphere in the atmosphere. Painting protection. The aliphatic polyurea anticorrosive coating of this product is an environmentally-friendly long-life heavy-duty anticorrosive coating developed in recent years. It has outstanding UV resistance and environmental protection. It is a high-solid and low-viscosity coating. The coating has high cross-linking density and shielding. It can effectively prevent the intrusion of corrosive factors in the environment, prolong the service life of the facility, and reduce the steel structure repair fees. polyaspartic vs polyurea
Performance characteristics polyaspartic coating
Using leading technology, high-performance aliphatic polyurea resin and aliphatic polyisocyanate are the main film-forming materials. The film-forming coating contains a large amount of urea bonds and a hydrogen bond structure, and has a high crosslinking density. These impart excellent barrier properties, abrasion resistance, chemical resistance, and UV resistance to the coating, and fully protect the metal structure from moisture and various external corrosion factors. The coating has a very high solid content, and can achieve zero VOC or very low VOC emission during the coating process. The required film thickness can be obtained in one construction, the construction efficiency is high, environmental protection and energy conservation. This product is suitable for the top coat layer of heavy-duty anti-corrosion coating. In addition to excellent protection performance, it also has ultra-long UV resistance (4000V resistance), and its UV resistance is comparable to that of fluorocarbon paint. More than traditional acrylic polyurethane (PU) coatings. Therefore, this type of coating has a wide range of applications in engineering vehicles, ships, wind power, hydraulic structures, offshore platforms and so on.
Technical Performance | Quick Information | ||
Adhesion | Level 1 | Density (film) | 1.1-1.25g/cm³ |
Impact Strength | ≥50kg.cm | Solid Content (%) | 80-95% |
Hardness | 2-3h | Construction Period(25℃) | ≥60min |
Flexibility | ≤1mm | Dry Film Thickness | 50-150μm |
Abrasion Resistance (750g/500r) | ≤0.03g | Theoretical Coverage | 0.15kg/m² (when dry film is 100µm) |
Salt Spray Resistance | 2000h | Surface Drying | 1h |
Water Resistance 30days | No corrosion, No bubble, No shedding | Actual Drying | 24h |
Acid Resistance 240h (5% H₂SO₄) | No corrosion, No bubble, No shedding | Actual Drying | 3-48h |
Salt Resistance 240h (3%NaCI) | No corrosion, No bubble, No shedding | Color | gray or specified color |
Alkali Resistance 240h (5%NaOH) | No corrosion, No bubble, No shedding | Luster | semi-dumb or light |
Oil Resistance 240h | No corrosion, No bubble, No shedding | Construction Methods | Brush, roller, airless spraying, spraying |
UV Resistant | 2000-4000h | | |
Alternating cycle of hot and cold (3 cycles) (One cycle: -20°Cx1h→80°Cx1h) | The paint film is intact, no abnormalities | | |
Water vapor permeability g / (m² d.kpa) | 0.007 | | |
Oxygen ion permeability mg/(cm².d) | 0.7x10﹣⁴ | | |
Mixing: Polyurea heavy anti-corrosion coating: curing agent = 100:50 (see packaging label for details)
T300 System Match plan
Epoxy zinc-rich primer: 50um epoxy cloud iron paint: 100-150um T300 topcoat: 50-150um
Waterproofing Application polyurea polyaspartic
Construction machinery, military equipment, oil storage tanks, wind power towers, offshore platforms, bridges, water gates and outdoor steel structures.
Shelf Life: The polyurea component is 12 months and the curing agent is 6 months (the product expires and the test can still be used).
Package: Polyurea coating 20kg Curing agent 10kg
Anti-corrosion layer construction process
Metal substrate blasting grade 2.5→epoxy zinc-rich primer (50um)→epoxy cloud iron coating (150um)→polyurea anticorrosive topcoat (50-150um)
Integrity statement: The company guarantees the authenticity of the listed data. Due to the diversity and variability of the product use environment, please demonstrate before use. We do not guarantee any responsibility other than the quality of the product itself. We reserve the right to modify the data provided without prior notice.
Polyaspartic coatings,We offer a mini sample kit and a money back guarantee.
Contact us if you need more details on T300 Polyurea Antiseptic Coating. We are ready to answer your questions on packaging, logistics, certification or any other aspects about T300 Polyurea Coating、T300 Antiseptic Coating. If these products fail to match your need, please contact us and we would like to provide relevant information.
Product Categories : Polyurea Waterproofing > UMS-AUPT Polyurea System